激光定向能量沉积与喷丸复合增材工艺，是以逐层喷丸的形式将喷丸表面强化原理与增材制造原理相结合，以达到降低工件缺陷和消除拉应力目的的一种复合工艺。比较该工艺机理与激光定向能量沉积工艺成形FeCrNiBSi合金试样的加工性能与质量，结果表明：复合工艺可将成形件表面的拉应力转变为压应力；与激光定向能量沉积工艺相比，复合工艺成形的试样密度提高了8.83%、表面粗糙度值降低了35.7%、拉伸强度与屈服强度分别提升了12.13%和53.24%。
Abstract：The laser directed energy deposition and shot peening composite additive process is a composite process that combines the shot peening surface strengthening principle with the additive manufacture in the form of layer by layer shot peening to reduce workpiece defects and eliminate tensile stress. Based on the mechanism of the process,the performance and quality of FeCrNiBSi alloy samples formed by the composite process and laser directed energy deposition process were compared.The result showed that the composite process could transform the tensile stress on the surface of the formed parts into the compressive stress. Compared with the laser directed energy deposition process,the sample density formed by the composite process increased by 8.83%,the surface roughness decreased by 35.7%,while the tensile strength and yield strength increased by 12.13% and 53.24%,respectively.
[1] KLBRYN P A,SEMIATIN S L. Mechanical properties of laser-deposited Ti-6Al-4V[J]. Solid Freeform Fabrication Proceedings,2001:6-8.
[2] LEUNDA J,SORIANO C,SANZ C,et al. Laser cladding of vanadium-carbide tool steels for die repair[J]. Physics Procedia,2011,12:345-352.
[3] LIU Q C,JANARDHANA M,HINTON B,et al. Laser cladding as a potential repair technology for damaged aircraft components[J]. International Journal of Structural Integrity,2011(3):314-331.
[4]崔爱永，胡芳友，张忠文，等.钛合金表面激光熔覆修复技术[J].中国表面工程，2011,24(2):61-64.
[5] DONOGHUE J,SIDHU J,WESCOTT A,et al. Integration of deformation processing with additive manufacture of Ti-6Al-4V components for improved β grain structure and texture[M]. Springer International Publishing,2015.
[6] ZHANG H O,WANG X P,WANG G L,et al. Hybrid direct manufacturing method of metallic parts using deposition and micro continuous rolling[J]. Rapid Prototyping Journal,2013,19(6):387-394.
[7] KALENTICS N,BOILLAT E,PEYRE P,et al. 3D laser shock peening-a new method for the 3D control of residual stresses in selective laser melting[J]. Materials and Design,2017,130:350-356.
[8] ZHANG X,LI D,ZHU W. Numerical modeling design for the hybrid additive manufacturing of laser directed energy deposition and shot peening forming Fe-Cr-Ni-B-Si alloy[J]. Materials,2020,13(21):4877.
[9]郑修麟.屈服强度与疲劳裂纹起始寿命间的关系[J].机械强度，1989,11(1):35-39.
基本信息:
中图分类号:TG66
引用信息:
[1]张晓宇,李涤尘,黄胜,等.激光定向能量沉积与喷丸复合工艺成形性能研究[J].电加工与模具,2022,No.370(05):45-47.
2022-10-20
2022-10-20